Kaiweite® S136h 718h P20h 738h Mask Maker Material KN95 Mask Maker Melt-Blown Fabric Rolling Mold is an improved steel grade of P20H mold steel(3Cr2Mo mold steel). which has greatly improved quality, making it Fill in the shortage of P20H mold steel and meet the requirements of P20H mold steel.
1. Product Introduction
Kaiweite® S136h 718h P20h 738h Mask Maker Material KN95 Mask Maker Melt-Blown Fabric Rolling Mold is an improved steel grade of P20H mold steel(3Cr2Mo mold steel). which has greatly improved quality, making it Fill in the shortage of P20H mold steel and meet the requirements of P20H mold steel.
Except that it cannot be used for plastic mold parts with corrosion resistance requirements, it is currently the most widely used mold steel.
The corporate upholds the philosophy of "Be No.1 in high quality, be rooted on credit history and trustworthiness for growth", will continue to serve previous and new customers from home and overseas whole-heatedly for Factory Directly supply China Kaiweite® S136h 718h P20h 738h Mask Maker Material KN95 Mask Maker Melt-Blown Fabric Rolling Mold, We have a professional team for international trade. We can solve the problem you meet. We can provide the products you want. Please feel free to contact us.
China High Quality Factory Directly supply Kaiweite® S136h 718h P20h 738h Mask Maker Material KN95 Mask Maker Melt-Blown Fabric Rolling Mold, Auto Mold Manufacturer, Welcome any of your inquiries and concerns for our items. We look forward to establishing a long-term business relationship with you in the near future. Contact us today. We have been the first business partner in your case!
|
Chemical Component %: |
|||||||
|
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
|
0.35 0.45 |
0.20 0.40 |
1.30 1.60 |
≤ 0.020 |
≤ 0.010 |
1.80 2.10 |
0.15 0.25 |
0.90 1.20 |
(1) 718H=P20H+1% Ni.
(2) The hardness of 718H steel is 4HRC higher than that of P20H.
(3) P20H is generally used as a less demanding plastic mold or plastic lower mold.718H Good polishing performance Generally used as a plastic mold with polishing requirements.
(4) The 718H die steel is in the annealed state at the factory and the hardness is HB290-310.
(5) The S136h 718h P20h 738h Mask Maker Material KN95 Mask Maker Melt-Blown Fabric Rolling Mold is in a pre-hardened state at the factory, and its hardness is HRC28-36.
2.Product Parameter (Specification)
|
Place of Origin: |
ningbo, China |
|
Application: |
Ship Plate |
|
Standard: |
AiSi, ASTM, bs, DIN, GB, JIS |
|
Width: |
2000-2300mm |
|
Length: |
2000-5800mm/3000-5800mm |
|
Grade: |
Carbon steel plate |
|
Tolerance: |
±10% |
|
Processing Service: |
Bending, Welding, Decoiling, Cutting, Punching |
|
Product Name: |
718,738,1.2738,718H |
|
MOQ: |
1Ton |
|
Shape: |
Round bars/steel sheets |
|
Certificate: |
ISO Certificate |
|
Technology: |
Hot Rolled/ Forged |
|
Keyword: |
718,738,1.2738,718H |
|
Experience: |
25 years manufacture experience |
|
Type: |
Steel Plate, Steel Plate |
|
Technique: |
Hot Rolled/Forged |
|
Surface Treatment: |
Black/Bright |
3.Product Feature And Application
1.Chemical composition(%)
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
|
0.47 - 0.55 |
0.17- 0.37 |
0.50 - 0.80 |
≤0.035 |
≤0.035 |
≤ 0.25 |
≤ 0.30 |
2. Equivalent Steel Grade
|
GB |
ASTM |
JIS |
|
50 |
1050 |
S50C |
3.Surface Treatment
Plate: Origin Black, Orign cold rolled bright, Machined, Grinded Round Bar: Origin Black, Orign cold rolled(drawn) bright, Turned, Peeled, Grinded
4.Characteristic
Medium-carbon high-strength carbon structural steel with high strength and hardness after quenching, the steel has mediummachinability, low cold deformation plasticity, poor weldability, no temper brittleness during heat treatment, but lowhardenability, and critical diameter in water 13 * 30mm, and there is a tendency to crack during water quenching. This steel isusually used after heat treatment such as normalizing or quenching and tempering, or high-frequency surface quenching.
5.Mechanical properties
Tensile strength σb (MPa): ≥630 (64)
Yield strength σs (MPa): ≥375 (38)
Elongation δ5 (%): ≥14
Section shrinkage ψ (%): ≥40
Impact energy Akv (J): ≥31 (4)
Impact strength value αkv (J/cm²): ≥39 (4)
Hardness: unheated, ≤241HB; annealed steel, ≤207HB